Nyocha zuru oke nke mkpara waya dị oke ike dị elu: Model Core, Parameters, yana Ngwọta Ngwa Multi-Scenario
Mkpanaka Waya Nkwado Structural Building Super High-Rise
Mkpara waya carbon dị ala (Q195/Q235):
● Ihe mejupụtara kemịkalụ: C ≤ 0.12% (Q195) / 0.14-0.22% (Q235), Mn 0.25-0.80%
● Nrụ ọrụ igwe: ike mpụta ≥195-235 MPa, ike ike 315-500 MPa, elongation ≥26-33%
● Ngwa: A na-ahazi ya site na eserese oyi ma ọ bụ ọgịrịga na-atụgharị n'ime rebar na electrodes nke ịgbado ọkụ, nke a na-ejikarị eme ihe maka nkwado siri ike na skyscrapers na àkwà mmiri.
mkpanaka waya etinyegoro SWRH82B:
● Ihe Ọdịnaya: C 0.80–0.85%, Mn 0.60–0.90%, Cr ≤0.25%
● Metrics siri ike: ike nkwụsị ≥1320 MPa, ike ≥1180 MPa, elongation ≥8%
● Ngwa: Zute ihe ndị chọrọ ibu ibu na ihe mgbochi seismic maka nnukwu ọrụ akụrụngwa.
Nkenke-nke-akpụpụta akụrụngwa ntọala ụlọ ọrụ
SWRH72A Mpempe eriri Carbon Steel Waya:
● Ihe mejupụtara kemịkalụ: C 0.70–0.75%, Si 0.15–0.35%, Mn 0.50–0.80%
● Mechanical Parameters: Ịkwụsị ike ≥1200 MPa, na-enye ike ≥900 MPa, Mbelata mpaghara ≥40%
● Ngwa: A na-eji eriri igwe igwe, isi iyi nkwusioru ụgbọ ala, na mmepụta ụdọ radial.
SAE1008 Oyi-isi igwe waya:
● Njikwa ihe: C 0.06-0.10%, Mn 0.30-0.50%, P/S ≤0.030%
● Metrics ductility: elongation ≥30%, mbelata mpaghara ≥65%
● Atụmatụ nhazi: Isi oyi dị elu maka ịmepụta bolts ike dị elu, bearings, na ngwaike akụrụngwa, na-eje ozi ụgbọ ala na ngwa ngwa ụlọ.
Mkpanaka waya Alloy pụrụ iche maka ọnọdụ dị oke egwu
30 CrMo Alloy Waya mkpanaka:
● Ihe mejupụtara Alloy: C 0.26–0.34%, Cr 0.80–1.10%, Mo 0.15–0.25%
● Arụmọrụ dị elu: ike mpụta ≥550 MPa na 550 ° C, ike ike ≥930 MPa na ụlọ okpomọkụ.
● Ngwa: Corrosion na okpomọkụ na-eguzogide wires ndị na-egwupụta mmanụ, ikuku turbine Tower arịlịka, na ihe mgbochi ikuku.
Osisi Waya Galvanized BZn18-18:
● Ihe ndabere: C ≤0.08%, Cu 0.25–0.40%, Zn 18–20%
● Ihe mkpuchi mkpuchi: Galfan® alloy mkpuchi (Zn-5% Al-RE), adhesion arọ 200-300 g/m²
● Nrụpụta: A na-etinye ya na eriri grid ọkụ na fencing nchebe maka gburugburu n'èzí.
Uru usoro yana ntuziaka nhọrọ ihe
Teknụzụ dị elu na-atụgharị na teknụzụ jụrụ oyi na-achịkwa na-eme ka o doo anya na nha nha (± 0.1 mm) na microstructural homogeneity, na-akwado usoro mgbada dị ka ịbịaru na ọgwụgwọ okpomọkụ. Nhọrọ ihe ga-agbasorịrị ụkpụrụ ụlọ ọrụ (ASTM, GB/T, JIS), na-ebute ọdịnaya carbon ụzọ, elongation, na njikwa ntụpọ elu.
Dị ka onye na-eweta mkpanaka waya zuru ụwa ọnụ, anyị na-ebuga ihe ngwọta zuru oke maka eriri ígwè, akụkụ ọkọlọtọ oyi na-atụ, na ihe waya alloy pụrụ iche, na-enye ndị ahịa ike iji belata ọnụ ahịa ma kwalite arụmọrụ. Kpọtụrụ anyị ugbu a maka katalọgụ ngwaahịa ahaziri ahazi na nkwado teknụzụ!
nkọwa2